LGHB 2/5 SKF Çok Yüksek Sıcaklık Basınç Viskozite Gres Yağı 5 KG
https://www.skf.com/binaries/pub12/Images/0901d19680063456-12050EN_LGHB2_tcm_12-31123.pdf
Designation | LGHB 2/(pack size) | |
DIN 51825 code | KP2N-20 | |
NLGI consistency class | 2 | |
Thickener | Calcium sulphonate complex | |
Colour | Brown | |
Base oil type | Mineral | |
Operating temperature range | –20 to +150 °C (–5 to +300 °F) | |
Dropping point DIN ISO 2176 | >220 °C (>430 °F) | |
Base oil viscosity | 40 °C, mm²/s | 400–450 |
100 °C, mm²/s | 26,5 | |
Penetration DIN ISO 2137 | 60 strokes, 10–1 mm | 265–295 |
100 000 strokes, 10–1 mm | –20 to +50 (325 max.) | |
Mechanical stability | Roll stability, 72 hrs at 100 °C, 10–1 mm | –20 to +50 change |
V2F test | ‘M’ | |
Corrosion protection | Emcor: – standard ISO 11007 | 0–0 |
Emcor: – water washout test | 0–0 | |
Emcor: – salt water test (100% seawater) | 0–0* | |
Water resistance | DIN 51 807/1, 3 hrs at 90 °C | 1 max. |
Oil separation | DIN 51 817, 7 days at 40 °C, static, % | 1–3 at 60 °C (140 °F) |
Lubrication ability | R2F, running test B at 120 °C | Pass at 140 °C (285 °F) |
Copper corrosion | DIN 51 811 | 2 max. 150 °C (300 °F) |
Rolling bearing grease life | R0F test L50 life at 10 000 r/min., hrs | >1 000 at 130 °C (265 °F) |
EP performance | Wear scar DIN 51350/5, 1 400 N, mm | 0,86* |
4–ball test, welding load DIN 51350/4, N | 4 000 min. | |
Fretting corrosion | ASTM D4170 (mg) | 0* |
Shelf life | 5 years | |
* Typical value |