LGET 2/1 SKF

• Long life in aggressive environments such as very reactive environments or areas with a presence of high purity gaseous oxygen, hexane and so on
• Excellent oxidation resistance
• Good corrosion resistance
• Excellent water and steam resistance

Available pack sizes

• 50 g (25 ml) syringe
• 1 kg can

Technical data

• DIN 51825 code : KFK2U-40
• NLGI consistency class : 2
• Soap type : PTFE
• Colour : whitish cream
• Base oil type : synthetic (fluorinated polyether)
• Operating temperature range, °C (°F) : -40 to 260 (-40 to 500)
• Dropping point DIN ISO 2176, °C (°F) : >300 (572)
• Base oil viscosity
  • 40 °C, mm2/s : 400
  • 100 °C,mm2/s : 38
• Penetration DIN ISO 2137
  • 60 strokes, 10-1 mm : 265-295
  • 100,000 strokes, 10-1 mm : –
• Mechanical stability
  • Roll stability, 50 hours at 80 °C, change 10-1 mm : ±30 max. (130 °C/266 °F)
  • Roll stability, 72 hours at 100 °C, change 10-1 mm : –
  • SKF V2F test : –
• Corrosion protection SKF Emcor:
  • standard ISO 11007 : 0 – 1
  • water washout test : –
  • salt water test (100% seawater) : –
• Water resistance
  • DIN 51 807/1, 3 hrs at 90 °C : 1 max.
• Oil separation
  • DIN 51 817, 7 days at 40 °C, static, % : 2 – 3
• Lubricating ability
  • SKF R2F, running test B : –
• Copper corrosion
  • DIN 51 811, 100 °C : 1 (150 °C/300 °F)
• Rolling bearing grease life
  • SKF R0F test L50 life at 10 000 rpm, hrs : >700, 5600 rpm at 220 °C (428 °F)
• EP performance
  • Wear scar, DIN 51350/5, 1400 N, mm : –
  • 4 ball test, welding load, DIN 51350/4 : 4000 min.
• Designation : LGET 2/0.05

Important note: Fluorinated greases in general are very costly, however LGET 2 is competitively priced. Given that LGET 2 is more expensive than other SKF greases, it is therefore recommended to use it only for applications where other SKF greases would not provide the required performance.